Our Hot Dipped Galvanized Steel is produced on a state of art, computer controlled production line. The best available raw materials and processes are applied under controlled conditions to produce material of high quality.
Our manufacturing facility, a dynamic production team and adherence to strict quality control measures ensures a product of the highest grade.
The state-of-the-art facility comprises of a non-oxidizing furnace with a continuous galvanizing line from some of the top suppliers in the world such as Tenova, and Ajax-Toco.
Currently ISL has the capability of producing over 400,000MT of Galvanized products.
Cold rolled steel sheet is cleaned and annealed in a continuous NOX furnace before being immersed in a molten zinc bath under an inert atmosphere. The molten zinc forms a metallurgical bond with the steel and protects the substrate by a sacrificial protection mechanism; the zinc sacrifices itself to protect the steel against corrosion.
Our products are produced as per:
- JIS G3302 and equivalent
|Type||Grade||Applicable nominal thickness (mm)||Zinc Coating|
|0.15 to 2.50||Z05 to Z27|
Standard Nominal Widths
Our Standards widths include 914mm, 1,000mm and 1,219mm. Other Widths and Thicknesses can be made available on request.
Quality Assurance Tests
|Quality Tests Performed||Equipment|
|Zinc coating mass in line||Jasch gauge.|
|Zinc coating mass laboratory||Weigh scale, Glass ware, Sample punch.|
|Chromate analysis (Passivator)||Chemical analysis.|
|Zinc Pot chemistry Analyzer||Spectormax.|
|Coating adhesion test||T bend tester.|
|Fluting test||Fluting tester.|
|Tensile test||Universal tensile testing machine.|
|Yield point test||Universal tensile testing machine.|
|Elongation test||Universal tensile, testing machine, Vernier Caliper.|
|Hardness test||Rockwell hardnesstester, Vickers hardness tester.|
|Base metal thickness||Micrometer.|
|Strip width||Measuring tape.|
|Strip Flatness||Surface Plate.|
|Surface defects||Strobe light for inspection, Visual Inspection, top and bottom of moving strip.|
|Cupping test||Cupping Test Machine.|
|Strip sampling||Strip bench shear.|
Cladding/Sliding, roofing, building accessories, sliding shutters, doors, partitions, canopies of gas stations, false ceilings, pre-fabricated buildings, sandwich panels, HVAC(heating, ventilation & air con ducting) etc.
Washing Machines, gas ovens, microwave ovens, refrigerators, freezers coolers, elevator, vending machines, grillers, toasters, air conditioners etc.
Doors, fenders, heat insulators, air cleaners, air conditioners etc.
Water tanks, trunks, canisters, ducting, water coolers, Ice boxes, geysers, etc.
Containers, packaging, furniture, computer peripherals, road signs, bus body buildings, storage bins, bill boards, etc.
Hot Dipped Galvanizing increases the life of cold rolled material by many years under extreme weather conditions.
The coating thicknesses are regular, predictable and easily specified.
Because it is dipped in molten zinc the entire surface of the base metal is coated uniformly.
In hot dipped galvanizing there is a structural bond between zinc and iron. It’s not just a coating but the zinc itself becomes a part of steel giving it a long lasting protection against corrosion. Strong adhesion with the base metal besides service life gives good formability in subsequent manufacturing processes.
Galvanizing is the cheapest in long term maintenance.
- It weathers at a slower rate giving it a long and predictable life.
- The coating sacrifices itself to any small areas exposed through drilling, cutting or accidental damage.